PENGARUH SERAT WARU (Hibiscus Tiliaceus) TERHADAP KARAKTERISTIK MORTAR GEOPOLIMER BATU NAPAL
Main Article Content
Abstract
This study discusses the addition of hibiscus fiber to the characteristics of marl geopolymer mortar. Geopolymer Mortar is a mortar with a binder that completely does not use cement as a binder. The research method used was alkaline activator NaOH and Na2SiO3 with a ratio of 1: 1 and a molarity of 16 M. The percentage of fiber addition used was 0%, 0.5% and 1.5% of the weight of the precursor and the length of the fiber was 2 cm. All specimens were tested for compressive strength at the age of 3, 7, 14, 21 and 28 days. The results of the research that have been carried out, it was found that the compressive strength at the age of 28 days with 0% fiber proportion was 3.07 Mpa. Meanwhile, the proportion of 0.5% fiber is 2.53 MPa and the proportion of 1.5% fiber is 2.27 MPa
Article Details
Section
Articles
References
Aditama, V., Amaral, B., & Hidayat, S. (2015). Pola Keruntuhan Dan Peningkatan Struktur Dinding Dengan Mortar Serat Kelapa. 34-42.
Aditama, V., Amaral, B., & Hidayat, S. (2021). Pola Keruntuhan Dan Peningkatan Kekuatan Pada Struktur Dinding Dengan Mortar Serat Kelapa. 34-42.
Amna, K., Wesli, & Hamzani. (2014). Pengaruh Penambahan Serat Tandan Sawit Terhadap Kuat Tekan Dan Kuat Lentur Beton. Teras Jurnal, Vol.4, No.2, 11-20.
ASTM C270. (2017). Standard Specification for Mortar For Unit Masonry. U.S Defartment Of Difense.
Chand, N., Tiwary, R., & Rohatgi, P. (381-387). Bibliography Resource structure properties of natural cellulosic fibres — an annotated bibliography. Journal Of Materials Science, 1998.
El-Habaak, G., Askalany, M., & Abdel-Hakeem, M. (2018). building up and characterization of calcined marl-based geopolymeric cement. infrastructures, 1-14.
Fadhillah, A. R., Hermawan, D., & Wardhani, A. R. (2019). Pengaruh Prosentase Larutan Naoh Pada Proses Alkalisasi Serat Kulit Pohon Waru (Hibiscus Tiliaceus) Sebagai Reinforcement Komposit Terhadap Kekuatan Tarik Serat Tunggal. Jurnal Program Studi Teknik Mesin UM Metro, 112.
Fajri. (2020). Pengaruh Penambahan Serat Tali Rafia Terhadap Sifat Mekanis Mortar Geopolimer. Portal Jurnal Teknik Sipil, 73-80.
Fitri, J., Olivia, M., & Romey s., I. (2016). Perancngan Mortar Geopolimer Abu Sekam. Jom FTEKNIK, 1-8.
Hardjito, D., Wallah, S. E., Sumanjouw, D. M., & Rangan, B. V. (2004). On The Devolopment OF Fly Ash- Based Geopolymer Concrite. Aci Materials Journal, 467-472.
Harsoyo, Y. A., & Fauzi, M. R. (2021). Pengaruh Penmabahan Serat Limbah Plastik HPDE Terhadap Kuat Tekan Pada Mortar. ISSN, 62-64.
Istiqomah. (2013). Workability Dan Kuat Tekan Mortar Sabut Kelapa. Seminar Nasional III Teknik Sipil, 41-45.
Junaidi, I. (2018). Pengaruh Penambahan Abu Sekam Padi dan Serbuk Genteng Press Terhadap Semen Geopolimer Berbahan Dasar Fly-Ash Aktivator (NaOH) dan Katalisator (Na2SiO3). Jurnal Online Universitas Jember Vol 2 No 4, 33-43.
Khoiriyah, N. L., & Maiysitoh, P. (2016). Karakteristik Mortar Geopolimer Dengan Perawatan Open Pada Berbagai Variasi Waktu Curing. Politeknologi , 1-8.
Kusumastuti, A. (2009). Aplikasi Serat Sisal tehadap komposit polimer. Jurnal Kompetisi Teknik, 27-32.
Manuahe , R., Sumajouw, D. M., & Windah, R. (2014, September 6). Kuat Tekan Beton Geopolimer Berbahan Dasar Abu Terbang (Fly Ash). Jurnal Sipil Statik, 277-282.
Mufida, A., Suprayogi, M. R., & Azwar, E. (2018). Analisis Reduksi Suara Dan Kuat Tarik Komposit Beton Serat Gedebok Pisang Hasil Delignifikasi Dengan Pelarut Natrium Hidroksida (Naoh). Journalbalitbangdalampung, 106.
Pradipta, Y. (2014, 05). http://yusufprdpt.blogspot.com. Diambil kembali dari http://yusufprdpt.blogspot.com.
Prasetyo, A., Purwanto, H., & Respati, S. B. (2016). Pengaruh Waktu Perendaman Serat Kulit Pohon Waru (Hibiscus Tiliaceus) Pada Air Laut Terhadap Struktur Mikro Dan Kekuatan Tarik. Momentum, Vol. 12, No. 2, 42-47.
Prayuda , H., & Pujianto, A. (2018). Kuat Tekan Beton Mutu Tinggi Menggunakan Komparasi Agregat Gamalama, Agregat Merapi Dan Agregat Kali Progo. Jurnal Riset Rekayasa Sipil.
Purwanto, E., Kristiawan, S., & Prabaswara, D. (2020). Pengaruh Variasi Anyaman Lateral Serat Cantula (Agave Cantula ROXB) Pada Textile Reinforced Concrete (TRC) Terhadap Kuat Tekan Beton. Jurnal Mattriks Teknik Sipil, 15-21.
Rianto, A., Soeparman, S., & Sugiarto. (2011). Karakterisasi Kekuatan Bending Dan Hidrofobisitas Komposit Serat Kulit Waru (Hibiscus Tiliaceus) Kontinyu Bermatrik Pati Ubi Kayu. Jurnal Rekayasa Mesin Vol.2, 130- 136.
Robinson, T. (1995). Kandungan Organik Tumbuhan Tinggi. Institut Teknologi Bandung.
Rozi, M. F., Tarigan, J., & Perwira, A. (2020). Analisis Sifat Mekanik Beton Geopolymer Berbahan Dasar
Aditama, V., Amaral, B., & Hidayat, S. (2021). Pola Keruntuhan Dan Peningkatan Kekuatan Pada Struktur Dinding Dengan Mortar Serat Kelapa. 34-42.
Amna, K., Wesli, & Hamzani. (2014). Pengaruh Penambahan Serat Tandan Sawit Terhadap Kuat Tekan Dan Kuat Lentur Beton. Teras Jurnal, Vol.4, No.2, 11-20.
ASTM C270. (2017). Standard Specification for Mortar For Unit Masonry. U.S Defartment Of Difense.
Chand, N., Tiwary, R., & Rohatgi, P. (381-387). Bibliography Resource structure properties of natural cellulosic fibres — an annotated bibliography. Journal Of Materials Science, 1998.
El-Habaak, G., Askalany, M., & Abdel-Hakeem, M. (2018). building up and characterization of calcined marl-based geopolymeric cement. infrastructures, 1-14.
Fadhillah, A. R., Hermawan, D., & Wardhani, A. R. (2019). Pengaruh Prosentase Larutan Naoh Pada Proses Alkalisasi Serat Kulit Pohon Waru (Hibiscus Tiliaceus) Sebagai Reinforcement Komposit Terhadap Kekuatan Tarik Serat Tunggal. Jurnal Program Studi Teknik Mesin UM Metro, 112.
Fajri. (2020). Pengaruh Penambahan Serat Tali Rafia Terhadap Sifat Mekanis Mortar Geopolimer. Portal Jurnal Teknik Sipil, 73-80.
Fitri, J., Olivia, M., & Romey s., I. (2016). Perancngan Mortar Geopolimer Abu Sekam. Jom FTEKNIK, 1-8.
Hardjito, D., Wallah, S. E., Sumanjouw, D. M., & Rangan, B. V. (2004). On The Devolopment OF Fly Ash- Based Geopolymer Concrite. Aci Materials Journal, 467-472.
Harsoyo, Y. A., & Fauzi, M. R. (2021). Pengaruh Penmabahan Serat Limbah Plastik HPDE Terhadap Kuat Tekan Pada Mortar. ISSN, 62-64.
Istiqomah. (2013). Workability Dan Kuat Tekan Mortar Sabut Kelapa. Seminar Nasional III Teknik Sipil, 41-45.
Junaidi, I. (2018). Pengaruh Penambahan Abu Sekam Padi dan Serbuk Genteng Press Terhadap Semen Geopolimer Berbahan Dasar Fly-Ash Aktivator (NaOH) dan Katalisator (Na2SiO3). Jurnal Online Universitas Jember Vol 2 No 4, 33-43.
Khoiriyah, N. L., & Maiysitoh, P. (2016). Karakteristik Mortar Geopolimer Dengan Perawatan Open Pada Berbagai Variasi Waktu Curing. Politeknologi , 1-8.
Kusumastuti, A. (2009). Aplikasi Serat Sisal tehadap komposit polimer. Jurnal Kompetisi Teknik, 27-32.
Manuahe , R., Sumajouw, D. M., & Windah, R. (2014, September 6). Kuat Tekan Beton Geopolimer Berbahan Dasar Abu Terbang (Fly Ash). Jurnal Sipil Statik, 277-282.
Mufida, A., Suprayogi, M. R., & Azwar, E. (2018). Analisis Reduksi Suara Dan Kuat Tarik Komposit Beton Serat Gedebok Pisang Hasil Delignifikasi Dengan Pelarut Natrium Hidroksida (Naoh). Journalbalitbangdalampung, 106.
Pradipta, Y. (2014, 05). http://yusufprdpt.blogspot.com. Diambil kembali dari http://yusufprdpt.blogspot.com.
Prasetyo, A., Purwanto, H., & Respati, S. B. (2016). Pengaruh Waktu Perendaman Serat Kulit Pohon Waru (Hibiscus Tiliaceus) Pada Air Laut Terhadap Struktur Mikro Dan Kekuatan Tarik. Momentum, Vol. 12, No. 2, 42-47.
Prayuda , H., & Pujianto, A. (2018). Kuat Tekan Beton Mutu Tinggi Menggunakan Komparasi Agregat Gamalama, Agregat Merapi Dan Agregat Kali Progo. Jurnal Riset Rekayasa Sipil.
Purwanto, E., Kristiawan, S., & Prabaswara, D. (2020). Pengaruh Variasi Anyaman Lateral Serat Cantula (Agave Cantula ROXB) Pada Textile Reinforced Concrete (TRC) Terhadap Kuat Tekan Beton. Jurnal Mattriks Teknik Sipil, 15-21.
Rianto, A., Soeparman, S., & Sugiarto. (2011). Karakterisasi Kekuatan Bending Dan Hidrofobisitas Komposit Serat Kulit Waru (Hibiscus Tiliaceus) Kontinyu Bermatrik Pati Ubi Kayu. Jurnal Rekayasa Mesin Vol.2, 130- 136.
Robinson, T. (1995). Kandungan Organik Tumbuhan Tinggi. Institut Teknologi Bandung.
Rozi, M. F., Tarigan, J., & Perwira, A. (2020). Analisis Sifat Mekanik Beton Geopolymer Berbahan Dasar